How to Minimize Environmental Paint Damage
The paintwork on your Mazda represents the latest technical developments in composition and methods of application.
Environmental hazards, however, can harm the paint's protective properties, if proper care is not taken.
Here are some examples of possible damage, with tips on how to prevent them.
Etching Caused by Acid Rain or Industrial Fallout
Occurrence
Industrial pollutants and vehicle emissions drift into the air and mix with rain or dew to form acids. These acids can settle on a vehicle's finish. As the water evaporates, the acid becomes concentrated and can damage the finish.
And the longer the acid remains on the surface, the greater the chance is for damage.
Prevention
It is necessary to wash and wax your vehicle to preserve its finish according to the instructions in this section. These steps should be taken immediately after you suspect that acid rain has settled on your vehicle's finish.
Damage Caused by Bird Dropping, Insects, or Tree Sap
Occurrence
Bird droppings contain acids. If these aren't removed they can eat away the clear and color base coat of the vehicle's paintwork.
When insects stick to the paint surface and decompose, corrosive compounds form. These can erode the clear and color base coat of the vehicle's paintwork if they are not removed.
Tree sap will harden and adhere permanently to the paint finish. If you scratch the sap off while it is hard, some vehicle paint could come off with it.
Prevention
It is necessary to have your Mazda washed and waxed to preserve its finish according to the instructions in this section. This should be done as soon as possible.
Bird droppings can be removed with a soft sponge and water. If you are traveling and these are not available, a moistened tissue may also take care of the problem.
The cleaned area should be waxed according to the instructions in this section.
Insects and tree sap are best removed with a soft sponge and water or a commercially available chemical cleaner.
Another method is to cover the affected area with dampened newspaper for one to two hours. After removing the newspaper, rinse off the loosened debris with water.
Water Marks
Occurrence
Rain, fog, dew, and even tap water can contain harmful minerals such as salt and lime. If moisture containing these minerals settles on the vehicle and evaporates, the minerals will concentrate and harden to form white rings. The rings can damage your vehicle's finish.
Prevention
It is necessary to wash and wax your vehicle to preserve its finish according to the instructions in this section. These steps should be taken immediately after you find water marks on your vehicle's finish.
Paint Chipping
Occurrence
Paint chipping occurs when gravel thrown in the air by another vehicle's tires hits your vehicle.
How to avoid paint chipping
Keeping a safe distance between you and the vehicle ahead reduces the chances of having your paint chipped by flying gravel.
NOTE:
- The paint chipping zone varies with the
speed of the vehicle. For example, when
traveling at 90 km/h (56 mph), the paint
chipping zone is 50 m (164 ft).
- In low temperatures a vehicle's finish hardens. This increases the chance of paint chipping.
- Chipped paint can lead to rust forming on your Mazda. Before this happens, repair the damage by using Mazda touch-up paint according to the instructions in this section.
Failure to repair the affected area could lead to serious rusting and expensive repairs.
See also:
Distributor in Each Area
CANADA
Mazda Canada Inc.
55 Vogell Road, Richmond Hill,
Ontario, L4B 3K5 Canada
TEL: 1 (800) 263-4680 (in Canada)
(905) 787-7000 (outside Canada)
PUERTO RICO/U.S. Virgin Island
Plaza Motors Cor ...
Advanced Key Suspend Function
If an advanced key is left in the vehicle,
the functions of the advanced key left in
the vehicle are temporarily suspended to
prevent theft of the vehicle.
The following are inoperable:
- Startin ...
Zoom-Zoom Handling
The Mazda CX9 body shell has a highly rigid structure in the lower body with
multiple cross members under the floor, a reinforced upper body area at the
C-pillar, a high-tensile steel B-pillar and ...